Loctite3D LOCTITE 3D IND6845 Resin - Black - (1kg) 1 Case - 24 units
LOCTITE 3D IND6845 Resin is a tough, high-performance industrial resin with a moderately high Heat Deflection Temperature (up to 80°C) and excellent impact resistance. It creates finely detailed, smooth-surfaced parts and is TPO-free for enhanced safety. Ideal for jigs, tooling, fixtures, and end-use plastic parts.
- High heat resistance up to 80C
- Outstanding impact resistance and durability
- Smooth, finely detailed surface finish
To learn about available discounts, training, and maintenance options, please use the form below and a MatterHackers Expert will contact you within one business day. Alternatively, you can always feel free to give us a call at +1 (800) 613-4290 or email sales@matterhackers.com.
To get an instant quote, add everything you need to your cart, and click "Download as quote".
LOCTITE 3D IND6845 RESIN
Tough, High-Performance Resin for Industrial Applications
LOCTITE 3D IND6845 delivers a unique combination of moderately high Heat Deflection Temperature (HDT) and outstanding toughness, making it ideal for industrial and end-use applications. Its ability to produce parts with smooth surfaces, fine details, and excellent impact resistance ensures durability in components exposed to mechanical stress and wear. TPO-free and boasting improved printability, this black resin prioritizes safety and efficiency in manufacturing environments.
Key Features of the LOCTITE 3D IND6845 RESIN:
- Moderately High HDT: Handles temperatures up to 80°C with reliable performance.
- Tough and Durable: Excellent impact resistance for parts exposed to mechanical stress.
- Smooth Surface Finish: Produces finely detailed parts with precision.
- TPO-Free Composition: Enhances safety ratings in industrial settings.
- Versatile Applications: Perfect for jigs, tooling, fixtures, and general end-use plastic parts.
Performance and Safety with LOCTITE 3D IND6845
LOCTITE 3D IND6845 offers a unique balance of moderately high Heat Deflection Temperature (HDT) and toughness, delivering smooth surfaces and fine details. Its excellent impact resistance and TPO-free composition make it ideal for high-wear components while ensuring improved safety in manufacturing environments.
- Combines toughness and impact resistance for durability in demanding applications.
- Produces parts with smooth surfaces and precise details.
- TPO-free formulation enhances health and safety standards in industrial use.
Safety and Versatility with LOCTITE 3D IND6845
LOCTITE 3D IND6845 is a TPO-free resin that enhances safety standards in manufacturing environments while offering an excellent balance of Heat Deflection Temperature (HDT) and toughness. With increased print speed and versatility, it is ideal for a wide range of industrial and end-use applications.
- TPO-free composition ensures improved health and safety ratings.
- Combines high HDT and toughness for durability in demanding environments.
- Optimized for jigs, tooling, fixtures, and general industrial applications.
Workflow for LOCTITE 3D IND6845
To achieve the material properties specified in the technical data sheet (TDS), it is essential to follow validated workflows. Always consult the latest workflow information and adhere to safety guidelines for optimal results.
Printer Settings
- Printer Compatibility: Optimized for DLP and LCD printers.
- Preparation: Shake the resin bottle thoroughly before use.
- Operating Temperature: Maintain a print environment between 20°C to 35°C.
- Light Intensity: Recommended settings range from 1.5 mW/cm² to 5 mW/cm².
Refer to the safety data sheet (SDS) for detailed health and safety instructions prior to use.
Properties of LOCTITE 3D IND6845
The mechanical, thermal, and electrical properties of LOCTITE 3D IND6845 are outlined below. These values represent both green and post-processed states, ensuring reliability for various industrial applications.
Mechanical Properties
- Young’s Modulus (MPa):
- Green: 1680 – 1830
- Post-Processed: 1980 – 2200
- Tensile Stress at Yield (MPa):
- Green: 41 – 43
- Post-Processed: 55 – 59
- Elongation at Yield (%):
- Green: 4.1 – 4.6
- Post-Processed: 4.4 – 5.6
- Tensile Stress at Break (MPa):
- Green: 32 – 34
- Post-Processed: 47 – 49
- Elongation at Break (%):
- Green: 56 – 64
- Post-Processed: 35 – 45
- Flexural Modulus (MPa):
- Post-Processed: 1960 – 2300
- Flexural Stress at Break (MPa):
- Post-Processed: 80 – 95
- Flexural Elongation at Break (%):
- Post-Processed: >5
- IZOD Impact (Notched) (J/m):
- Post-Processed: 28 – 35
- Shore Hardness (3s) (D):
- Post-Processed: 81 – 83
Thermal Properties
- HDT at 0.455 MPa (°C): 80 – 85
- HDT at 1.82 MPa (°C): 62 – 68
- Thermal Conductivity (W/(m·K)): 0.20 – 0.21
- Heat Capacity (J/(g·K)): 1.2 – 1.3
Liquid Properties
- Viscosity at 25°C (cP): 719 – 769
- Liquid Density (g/cm³): 1.07
Electrical Properties
- Volume Resistivity (Ω·cm): 5.1E+15 – 3.7E+15
- Surface Resistivity (Ω): 9.9E+15 – 8.1E+15
- Dielectric Strength (kV/mm): 14.4 – 13.8
For additional property details or pending results, refer to the technical data sheet (TDS).