Loctite3D LOCTITE 3D PRO9317 Resin - Clear - 1kg
LOCTITE 3D PRO9317 Resin delivers high clarity with balanced tensile and flexural properties and low viscosity for smooth, bubble-free printing. It withstands moderate heat and mechanical stress, making it suitable for applications such as detailed packaging, wearable prototypes, and lighting components.
- Produce transparent parts with fine details
- Ensure durable, impact-resistant performance consistently
- Accelerate printing with low viscosity flow
| List Price: | $120.00 |
|---|---|
| Price: | $120.00 |
| Price: | $... |
| Availability: | In Stock |
| Order Now: | Ships Monday Free U.S. Shipping |
LOCTITE 3D PRO9317 Resin
High-Clarity Resin for Detailed Prototyping
LOCTITE 3D PRO9317 Resin is a high-clarity material designed for precision prototyping and end-use applications that demand fine feature detail. This advanced resin delivers exceptional transparency, enabling the production of high-quality parts such as detailed packaging, wearable prototypes, and lighting components. With optimized mechanical properties, LOCTITE 3D PRO9317 ensures durability, impact resistance, and thermal stability, making it a versatile choice for a wide range of industries. Its low viscosity allows for smooth, bubble-free printing, and its balanced tensile and flexural properties provide strong, reliable performance.
Key Features of the LOCTITE 3D PRO9317 Resin:
- Exceptional Clarity: Produces highly transparent parts with fine feature detail.
- Strong Mechanical Properties: Offers high tensile and flexural strength for durable prints.
- Impact & Thermal Resistance: Withstands mechanical stress and moderate heat exposure.
- Optimized for Fast Printing: Low viscosity enables smooth printing with minimal post-processing.
- Versatile Applications: Ideal for detailed packaging, wearable prototypes, and lighting solutions.
Technical Specifications
Basic Properties
- Young’s Modulus: 1358 MPa (ASTM D638)
- Ultimate Tensile Strength: 37 MPa (ASTM D638)
- Elongation at Break: 28% (ASTM D638)
Flexural Properties
- Flexural Modulus: 1467 MPa (ASTM D648)
- Flexural Stress: 57 MPa (ASTM D648)
Impact & Thermal Properties
- IZOD Impact (Notched): 47 J/m (ASTM D256)
- HDT at 1.82 MPa: 40°C (ASTM D648)
- HDT at 0.45 MPa: 47°C (ASTM D648)
General Properties
- Viscosity: 471 cP (ASTM D7876)
- Water Absorption (24hr): 0.24% (ASTM D570)
- Water Absorption (168hr): 0.59% (ASTM D570)
- Shore Hardness: 82D (ASTM D2240)
Printing Process
LOCTITE 3D PRO9317 Resin should be processed at room temperature. Shake well before use, pour slowly into the vat, and allow a few minutes for a smooth, bubble-free surface to form before printing.
For best results, users should optimize print settings based on their specific 3D printer and application requirements. Always refer to the printer’s user manual for detailed instructions on setup and handling.
Post-Processing & Washing
Printed parts require post-processing to achieve their full mechanical properties. Before curing, parts should be washed using an appropriate cleaning solution. Recommended cleaning process:
- Use xCLEAN for no longer than 2 minutes
- Follow with IPA rinse for no longer than 5 minutes
Extended exposure to cleaning agents may affect performance. Always follow best practices for post-processing to maintain part integrity.